Young's Modulus of Wurtzite and Zinc Blende InP Nanowires

Mikhail Dunaevskiy*, Pavel Geydt, Erkki Lähderanta, Prokhor Alekseev, Tuomas Haggrén, Joona Pekko Kakko, Hua Jiang, Harri Lipsanen

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

17 Sitaatiot (Scopus)

Abstrakti

The Young's modulus of thin conical InP nanowires with either wurtzite or mixed "zinc blende/wurtzite" structures was measured. It has been shown that the value of Young's modulus obtained for wurtzite InP nanowires (E[0001] = 130 ± 30 GPa) was similar to the theoretically predicted value for the wurtzite InP material (E[0001] = 120 ± 10 GPa). The Young's modulus of mixed "zinc blende/wurtzite" InP nanowires (E[111] = 65 ± 10 GPa) appeared to be 40% less than the theoretically predicted value for the zinc blende InP material (E[111] = 110 GPa). An advanced method for measuring the Young's modulus of thin and flexible nanostructures is proposed. It consists of measuring the flexibility (the inverse of stiffness) profiles 1/k(x) by the scanning probe microscopy with precise control of loading force in nanonewton range followed by simulations.

AlkuperäiskieliEnglanti
Sivut3441-3446
Sivumäärä6
JulkaisuNano Letters
Vuosikerta17
Numero6
DOI - pysyväislinkit
TilaJulkaistu - 14 kesäkuuta 2017
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Sormenjälki

Sukella tutkimusaiheisiin 'Young's Modulus of Wurtzite and Zinc Blende InP Nanowires'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä