XANES study on the evolution among different copper species, CuI, CuII and CuIII, in CuBa2YCu2O6+z upon oxygen loading

Y. Morita*, M. Karppinen, H. Yamauchi, R. S. Liu, J. M. Chen

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

3 Sitaatiot (Scopus)

Abstrakti

X-ray absorption near-edge structure (XANES) spectroscopy at the Cu L-edge is applied to follow the gradual formation of CUII and CuIII species from CuI with increasing amount of excess oxygen, z, in Cu(1) Ba2 YCu(2)2 O6+z. For the study, a series of samples with precisely controlled oxygen contents was prepared utilizing the temperature-controlled oxygen-depletion (TCOD) annealing technique in the sample synthesis and employing coulometric titration for accurate oxygen-content analysis. It may be concluded that at low amounts of excess oxygen, z, Cu(1)I in the charge reservoir tends to be first oxidized to Cu(1)II rather than directly to Cu(1) III, suggesting that complete chain formation does not occur at low oxygen contents.

AlkuperäiskieliEnglanti
Sivut1205-1210
Sivumäärä6
JulkaisuJournal of Low Temperature Physics
Vuosikerta131
Numero5-6
DOI - pysyväislinkit
TilaJulkaistu - kesäkuuta 2003
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Sormenjälki

Sukella tutkimusaiheisiin 'XANES study on the evolution among different copper species, Cu<sup>I</sup>, Cu<sup>II</sup> and Cu<sup>III</sup>, in CuBa<sub>2</sub>YCu<sub>2</sub>O<sub>6+z</sub> upon oxygen loading'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä