Wood densification and thermal modification: hardness, set-recovery and micromorphology

Tutkimustuotos: Lehtiartikkeli

Tutkijat

Organisaatiot

  • KTH Royal Institute of Technology
  • SP Technical Research Institute of Sweden

Kuvaus

The density of wood can be increased by compressing the porous structure under suitable moisture and temperature conditions. One aim of such densification is to improve surface hardness, and therefore, densified wood might be particularly suitable for flooring products. After compression, however, the deformed wood material is sensitive to moisture, and in this case, recovered up to 60 % of the deformation in water-soaking. This phenomenon, termed set-recovery, was reduced by thermally modifying the wood after densification. This study presents the influence of compression ratio (CR = 40, 50, 60 %) and thermal modification time (TM = 2, 4, 6 h) on the hardness and set-recovery of densified wood. Previously, set-recovery has mainly been studied separately from other properties of densified wood, while in this work, set-recovery was also studied in relation to hardness. The results show that set-recovery was almost eliminated with TM 6 h in the case of CR 40 and 50 %. Hardness significantly increased due to densification and even doubled compared to non-densified samples with a CR of 50 %. Set-recovery reduced the hardness of densified (non-TM) wood back to the original level. TM maintained the hardness of densified wood at an increased level after set-recovery. However, some reduction in hardness was recorded even if set-recovery was almost eliminated.

Yksityiskohdat

AlkuperäiskieliEnglanti
Sivut883–894
Sivumäärä12
JulkaisuWood Science and Technology
Vuosikerta50
Numero5
TilaJulkaistu - syyskuuta 2016
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

ID: 4663255