Water-Soluble Acrylate Binder for Graphite Electrodes in Lithium-Ion Batteries

Tutkimustuotos: Lehtiartikkeli

Tutkijat

Organisaatiot

  • Sun Chem Oy

Kuvaus

Water-soluble acrylate (AcrylS020) was tested as a potential binder for graphite negative electrodes in lithium-ion batteries, and the results were compared to the commonly used carboxymethyl cellulose (CMC) and styrene-butadiene rubber (SBR) CMC+SBR binder combination. Similar performance was observed at low C-rates and room temperature with both binders in Li/graphite half-cells. However, at high C-rates and/or low temperature, better results were obtained with AcrylS020 and the difference at room temperature and 1C was 166mAhg(-1) vs. 92mAhg(-1) (AcrylS020 vs. CMC+SBR). The stability of the electrodes was similar in graphite/NMC (LiNi1/3Mn1/3Co1/3O2) full-cell tests. The structures of the electrodes using different binders were slightly different as evidenced by SEM images. These results indicate that the AcrylS020 binder is also applicable for graphite negative electrodes and can tolerate the volume change of graphite during charging/discharging.

Yksityiskohdat

AlkuperäiskieliEnglanti
Sivut470-472
Sivumäärä3
JulkaisuEnergy Technology
Vuosikerta4
Numero4
TilaJulkaistu - huhtikuuta 2016
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

ID: 3243162