Wafer-Level AuSn/Pt Solid-Liquid Interdiffusion Bonding

Tutkimustuotos: Lehtiartikkelivertaisarvioitu

Tutkijat

Organisaatiot

  • VTT Technical Research Centre of Finland

Kuvaus

In this paper, wafer-level AuSn/Pt solid-liquid interdiffusion bonding for hermetic encapsulation of microelectromechanical systems (MEMS) is evaluated. Although AuSn is used for bonding of ICs, the implementation of AuSn diffusion bonding in MEMS applications requires thorough understanding of its compatibility with the complete layer stack including adhesion, buffer, and metallization layers. Partitioning of the layer stacks is possible in MEMS devices consisting of several silicon wafers since the device wafer carrying functional structures and the encapsulation wafer have different restrictions on process integration and applicable metal deposition techniques. In this paper, CMOS/MEMS compatible sputtered platinum is utilized on the device wafer as a contact metallization for Au-Sn metallized cap wafer. The role of the platinum layer thickness as well as the nickel and molybdenum buffer layers on mechanical reliability were tested. The mechanical shear and tensile tests were performed for samples after bonding as well as after high-temperature storage and thermal shock tests. The results were rationalized based on the combined microstructural, thermodynamic, and fracture surface analyses. High-strength and thermodynamically stable bonds were achieved, exhibiting shear strength up to $~ $180 MPa and tensile strength up to $~ $80 MPa. Platinum was consumed completely during bonding and was observed to dissolve mainly into the (Au,Pt)Sn phase. Thicker platinum layer (200 versus 100 nm) increased the (Au,Pt)Sn phase thickness and resulted in higher strength. The molybdenum buffer layer under the platinum metallization increased the tensile strength significantly.

Yksityiskohdat

AlkuperäiskieliEnglanti
Sivut169-176
JulkaisuIEEE Transactions on Components, Packaging and Manufacturing Technology
Vuosikerta8
Numero2
TilaJulkaistu - helmikuuta 2018
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Lataa tilasto

Ei tietoja saatavilla

ID: 17288866