Vacancy recovery and vacancy-hydrogen interaction in niobium and tantalum studied by positrons

P. Hautojarvi*, H. Huomo, M. Puska, A. Vehanen

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

56 Sitaatiot (Scopus)
135 Lataukset (Pure)

Abstrakti

Positron-lifetime measurements in electron-irradiated pure Nb and Ta show that monovacancy migration occurs at 220 and 260 K, respectively. Hydrogen impurities can be bound to vacancies, as is experimentally observed in Ta at 70 K after low-temperature ±-particle irradiation. The vacancy-hydrogen complex formation shifts the vacancy migration to higher temperatures. Vacancy hydrogen complexes retain the capability to trap positrons. Theoretical calculations performed for hydrogen and positron states at vacancies are in agreement with experimental findings.
AlkuperäiskieliEnglanti
Sivut4326-4331
Sivumäärä6
JulkaisuPhysical Review B
Vuosikerta32
Numero7
DOI - pysyväislinkit
TilaJulkaistu - 1 lokakuuta 1985
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Sormenjälki

Sukella tutkimusaiheisiin 'Vacancy recovery and vacancy-hydrogen interaction in niobium and tantalum studied by positrons'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä