Ultrathin-Walled 3D Inorganic Nanostructured Networks Templated from Cross-Linked Cellulose Nanocrystal Aerogels

Arto Hiltunen, Tyler Or, Kimmo Lahtonen, Harri Ali-Löytty, Nikolai Tkachenko, Mika Valden, Essi Sarlin, Emily D. Cranston, Jose M. Moran-Mirabal, Jaana Vapaavuori*

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

6 Lataukset (Pure)

Abstrakti

A key challenge in the development of materials for applications in the fields of opto- and nanoelectronics, catalysis, separation, and energy conversion is the ability to fabricate 3D inorganic semiconductive nanostructures in a precisely-controlled and cost-effective manner. This work describes the fabrication of 3D nanostructured TiO2 monoliths by coating ultraporous cross-linked cellulose nanocrystal (CNC) aerogel templates with TiO2 layers of controlled thickness via atomic layer deposition (ALD). Following calcination, the resulting hollow inorganic ultraporous 3D networks form the thinnest self-supporting semiconductive structure (7 nm) fabricated directly on a conductive substrate. The CNC-templated ALD–TiO2 electrodes are applied toward photoelectrochemical water splitting. The results show that a TiO2 coating as thin as 15 nm produces a maximum water splitting efficiency, resulting in materials savings and reduced fabrication time.

AlkuperäiskieliEnglanti
Artikkeli2001181
Sivumäärä6
JulkaisuAdvanced Materials Interfaces
Vuosikerta8
Numero11
Varhainen verkossa julkaisun päivämäärä7 toukokuuta 2021
DOI - pysyväislinkit
TilaJulkaistu - 9 kesäkuuta 2021
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Sormenjälki

Sukella tutkimusaiheisiin 'Ultrathin-Walled 3D Inorganic Nanostructured Networks Templated from Cross-Linked Cellulose Nanocrystal Aerogels'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä