Transparent conductive electrode based on LBL deposition of graphene oxide and copper nanowires

B. Tugba Camic, Jaana Vapaavuori*, Fevzihan Basarir*

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

5 Sitaatiot (Scopus)
44 Lataukset (Pure)

Abstrakti

In this work, Graphene/Copper Nanowire (G/CuNW) based transparent conducting electrodes (TCEs) were prepared via spin-assisted layer-by-layer (LBL) deposition. 3-aminopropyltriethoxysilane (ɣ-APS) functionalized glass substrates were sequentially spin-coated with graphene oxide (GO) and CuNWs. Then, to enhance the electrical conductivity, the multilayer films were subjected to chemical reduction and thermal annealing. The ultimate films were characterized by a scanning electron microscope, UV–Vis spectrometer, and sheet resistance using a four-point probe method. 3-bilayer G/CuNWs films exhibited sheet resistance of 9 Ω/sq and optical transmittance of 67% (at 550 nm), which is comparable to commercial ITO electrode in terms of mainly sheet resistance.

AlkuperäiskieliEnglanti
Artikkeli131632
Sivumäärä4
JulkaisuMaterials Letters
Vuosikerta311
Varhainen verkossa julkaisun päivämäärä29 jouluk. 2021
DOI - pysyväislinkit
TilaJulkaistu - 15 maalisk. 2022
OKM-julkaisutyyppiA1 Alkuperäisartikkeli tieteellisessä aikakauslehdessä

Sormenjälki

Sukella tutkimusaiheisiin 'Transparent conductive electrode based on LBL deposition of graphene oxide and copper nanowires'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä