Thermodynamic Stability of Condensed Phases in the Ternary System CaO-Cu-O by the EMF Method

Joseph Hamuyuni*, Dmitry Sukhomlinov, Mari Lundström, Pekka Taskinen

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: Artikkeli kirjassa/konferenssijulkaisussaConference article in proceedingsScientificvertaisarvioitu

Abstrakti

The standard thermodynamic properties of the compound Ca2CuO3 were determined electrochemically by the Electromotive Force (EMF) method. The ternary phase Ca2CuO3 was synthesized from the pure oxides CaO and CuO at CaO saturation using a ceramic route. The EMF measurements were performed over a temperature range 973Delta(f(ox))G degrees(Ca2CuO3) = 21.884-22.92 . 10(-3). T.

AlkuperäiskieliEnglanti
OtsikkoENERGY TECHNOLOGY 2017: CARBON DIOXIDE MANAGEMENT AND OTHER TECHNOLOGIES
ToimittajatL Zhang, JW Drelich, NR Neelameggham, DP Guillen, N Haque, J Zhu, Z Sun, T Wang, JA Howarter, F Tesfaye, S Ikhmayies, E Olivetti, MW Kennedy
KustantajaSpringer
Sivut79-86
Sivumäärä8
ISBN (elektroninen)978-3-319-52192-3
ISBN (painettu)978-3-319-52191-6
DOI - pysyväislinkit
TilaJulkaistu - 2017
OKM-julkaisutyyppiA4 Artikkeli konferenssijulkaisussa
TapahtumaEnergy Technologies Symposium - San Diego, Yhdysvallat
Kesto: 26 helmik. 20172 maalisk. 2017

Julkaisusarja

NimiMinerals Metals & Materials Series
KustantajaSPRINGER INT PUBLISHING AG
ISSN (painettu)2367-1181

Conference

ConferenceEnergy Technologies Symposium
Maa/AlueYhdysvallat
KaupunkiSan Diego
Ajanjakso26/02/201702/03/2017

Sormenjälki

Sukella tutkimusaiheisiin 'Thermodynamic Stability of Condensed Phases in the Ternary System CaO-Cu-O by the EMF Method'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä