Thermodynamic Assessment of Liquid Fe-Ni-C Alloy Using Modified Quasichemical Model

Min Paek, Junmo Jeon, Manas Paliwal, Arijit Biswas, Daniel Lindberg, Jong-Jin Pak

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

2 Sitaatiot (Scopus)
129 Lataukset (Pure)

Abstrakti

The liquid solution properties in the Fe-Ni and Fe-Ni-C systems have been thermodynamically assessed using the modified quasichemical model in the pair approximation. The asymmetry of the Fe-Ni and Fe-Ni-C alloy melts was verified by measuring the melting points of Fe-Ni binary alloys on the Ni-rich side, and the C solubility limit in Fe-Ni melt over the entire concentration range at 1500°C and 1600°C. The solubility minimum of C and the maximum partial enthalpy of mixing of C in the ternary Fe-Ni-C system occurred at near the maximum short-range ordering composition of the binary Fe-Ni liquid solution. The extrema of the partial properties of C in the ternary Fe-Ni-C system were successfully reproduced with only one constant adjustable ternary parameter.
AlkuperäiskieliEnglanti
Sivut679-687
Sivumäärä9
JulkaisuJOM
Vuosikerta73
Numero2
Varhainen verkossa julkaisun päivämäärä25 marrask. 2020
DOI - pysyväislinkit
TilaJulkaistu - helmik. 2021
OKM-julkaisutyyppiA1 Alkuperäisartikkeli tieteellisessä aikakauslehdessä

Sormenjälki

Sukella tutkimusaiheisiin 'Thermodynamic Assessment of Liquid Fe-Ni-C Alloy Using Modified Quasichemical Model'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.
  • SYMMET (TDM)

    Lindberg, D. (Vastuullinen tutkija), Attah-Kyei, D. (Projektin jäsen), Klemettinen, A. (Projektin jäsen), Jeon, J. (Projektin jäsen), Paek, M. (Projektin jäsen), Avarmaa, K. (Projektin jäsen) & Santoso, I. (Projektin jäsen)

    01/11/201831/10/2020

    Projekti: Business Finland: Other research funding

Siteeraa tätä