The Oxidation of Copper in Air at Temperatures up to 100 °C

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

177 Lataukset (Pure)

Abstrakti

The aim of this study was to investigate the oxidation kinetics of copper at low temperatures (60 °C to 100 °C) in air by isothermal thermogravimetric analysis (TGA) and quartz crystal microbalance (QCM). The weight change in thermogravimetric tests showed periodic weight increase and decrease. In thermogravimetric tests the mass of the copper sample increased until the oxidation gradually slowed down and finally started to decrease due to cracking and spalling of the oxide formed on the surface. In QCM tests using electrodeposited copper film, the weight change was rapid at the beginning but slowed to a linear relationship after few minutes. Temperature and exposure time appeared to have a large effect on oxide film thickness and composition. With QCM, oxidation at 60–80 °C produced less than 40 nm films in 10 days. Oxidation at 90–100 °C produced 40 nm thick films in a day and over 100 nm films in a week. Although SEM-EDS analyses in TGA tests indicated that oxygen was adsorbed on the copper surface, neither XRD patterns nor Raman spectroscopy measurements showed any trace of Cu2O or CuO formation on the copper surface. Electrochemical reduction analysis of oxidized massive copper samples indicated that the oxide film is mostly Cu2O, and CuO develops only after several days at 90–100 °C.
AlkuperäiskieliEnglanti
Sivut625-640
JulkaisuCorrosion and Materials Degradation
Vuosikerta2
Numero4
DOI - pysyväislinkit
TilaJulkaistu - 25 lokak. 2021
OKM-julkaisutyyppiA1 Alkuperäisartikkeli tieteellisessä aikakauslehdessä

Sormenjälki

Sukella tutkimusaiheisiin 'The Oxidation of Copper in Air at Temperatures up to 100 °C'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä