Synthesis and characterization of green urethane non-isocyanate from oleic acid for wood composite application

Muhammad Ghozali*, Samsul Bakhri, Evi Triwulandari, Witta Kartika Restu, Yenny Meliana, Agus Haryono, Melati Septiyanti, Nissa Nurfajrin Solihat, Seng Hua Lee, Widya Fatriasari, Petar Antov*

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

Abstrakti

Conventional polyurethane (PU) is usually synthesized by a reaction between isocyanate and polyol. The use of isocyanate compounds is associated with significant health and environmental problems. Therefore, it is necessary to develop an environmentally friendly alternative method for manufacturing PUs without isocyanate routes. The aim of this research work was to synthesize green urethane from oleic acid, which included the following three stages: the synthesis of epoxidized oleic acid (EOA), the synthesis of carbonated oleic acid (COA), and the synthesis of green urethane from oleic acid (UOA). The resulting product was characterized by Fourier Transform Infrared Spectroscopy (FTIR) and Nuclear Magnetic Resonance (NMR) analyses, and by determining the iodine number, oxirane number, and hydroxyl value. The results of FTIR and NMR showed that EOA was successfully synthesized. The optimum COA synthesis process was obtained on TBAB catalyst usage of 1% (wt/wt) at 140°C for 48 h with a 500-rpm stirring rate and CO2 gas flow rate of 0.2 mL/min with the resulting COA oxirane value of 0.00. The optimum condition of UOA synthesis through the aminolysis process resulted in the use of LiCl of 19.8% (wt/wt) at 70°C for 3 h with a stirring speed of 1200 rpm with a UOA hydroxyl number generated of 237.93 mg/mL.

AlkuperäiskieliEnglanti
Artikkelie54803
JulkaisuJournal of Applied Polymer Science
Vuosikerta141
Numero3
DOI - pysyväislinkit
TilaJulkaistu - 15 tammik. 2024
OKM-julkaisutyyppiA1 Alkuperäisartikkeli tieteellisessä aikakauslehdessä

Sormenjälki

Sukella tutkimusaiheisiin 'Synthesis and characterization of green urethane non-isocyanate from oleic acid for wood composite application'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä