Studies of the Electrochemical Behavior of LiNi0.80Co0.15Al0.05O2 Electrodes Coated with LiAlO2

Onit Srur-Lavi, Ville Miikkulainen, Boris Markovsky, Judith Grinblat, Michael Talianker, Yafit Fleger, Gili Cohen-Taguri, Albert Mor, Yosef Tal-Yosef, Doron Aurbach

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

24 Sitaatiot (Scopus)

Abstrakti

In this paper, we studied the influence of LiAlO2 coatings of 0.5, 1 and 2 nm thickness prepared by Atomic Layer Deposition onto LiNi0.8Co0.15Al0.05O2 electrodes, on their electrochemical behavior at 30 and 60 degrees C. It was demonstrated that upon cycling, 2 nm LiAlO2 coated electrodes displayed similar to 3 times lower capacity fading and lower voltage hysteresis comparing to bare electrodes. We established a correlation among the thickness of the LiAlO2 coating and parameters of the self-discharge processes at 30 and 60 degrees C. Significant results on the elevated temperature cycling and aging of bare and LiAlO2 coated electrodes at 4.3 V were obtained and analyzed for the first time. By analyzing of X-ray diffraction patterns of bare and 2 nm coated LiNi0.8Co0.15Al0.05O2 electrodes after cycling, we concluded that cycled materials preserved their original structure described by R-3m space group and no additional phases were detected. (c) The Author(s) 2017. Published by ECS. All rights reserved.

AlkuperäiskieliEnglanti
JulkaisuJournal of the Electrochemical Society
Vuosikerta164
Numero13
DOI - pysyväislinkit
TilaJulkaistu - 2017
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Sormenjälki Sukella tutkimusaiheisiin 'Studies of the Electrochemical Behavior of LiNi0.80Co0.15Al0.05O2 Electrodes Coated with LiAlO2'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä