Stability of gamma-valerolactone under pulping conditions as a basis for process optimization and chemical recovery

Marianna Granatier, Inge Schlapp-Hackl, Huy Quang Lê, Kaarlo Nieminen, Leena Pitkänen, Herbert Sixta*

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

1 Sitaatiot (Scopus)
62 Lataukset (Pure)

Abstrakti

This study focuses on the investigation of the extent of the γ-valerolactone (GVL) hydrolysis forming an equilibrium with 4-hydroxyvaleric acid (4-HVA) in aqueous solutions over a wide pH range. The hydrolysis of a 50 wt% GVL solution to 4-HVA (3.5 mol%) was observed only at elevated temperatures. The addition of sulfuric acid (0.2 × 10–5 wt% to 6 wt%) at elevated temperatures (150–180 °C) and reaction times between 30 and 180 min caused the formation of 4 mol% 4-HVA. However, with decreasing acidity, the 4-HVA remained constant at about 3 mol%. The hydrolysis reactions in alkaline conditions were conducted at a constant time (30 min) and temperature (180 °C) with the variation of the NaOH concentration (0.2 × 10–6 wt% to 7 wt%). The addition of less than 0.2 wt% of NaOH resulted in the formation of less than 4 mol% of sodium 4-hydroxyvalerate. A maximum amount of 21 mol% of 4-HVA was observed in a 7 wt% NaOH solution. The degree of decomposition after treatment was determined by NMR analysis. To verify the GVL stability under practical conditions, Betula pendula sawdust was fractionated in 50 wt% GVL with and without the addition of H2SO4 or NaOH at 180 °C and a treatment time of 120 min. The spent liquor was analyzed and a 4-HVA content of 5.6 mol% in a high acidic (20 kg H2SO4/t wood) and 6.0 mol% in an alkaline (192 kg NaOH/t wood) environment have been determined.

AlkuperäiskieliEnglanti
Sivut11567-11578
Sivumäärä12
JulkaisuCellulose
Vuosikerta28
Numero18
Varhainen verkossa julkaisun päivämäärä13 lokak. 2021
DOI - pysyväislinkit
TilaJulkaistu - jouluk. 2021
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Sormenjälki

Sukella tutkimusaiheisiin 'Stability of gamma-valerolactone under pulping conditions as a basis for process optimization and chemical recovery'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä