Slag–Copper Equilibria of Selected Trace Elements in Black Copper Smelting. Part I. Properties of the Slag and Chromium Solubility

Dmitry Sukhomlinov, Katri Avarmaa, Olli Virtanen, Pekka Taskinen*, Ari Jokilaakso

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

10 Sitaatiot (Scopus)
72 Lataukset (Pure)

Abstrakti

The solubility of chromium in alumina- and lime-containing (≈5 wt% Al 2 O 3 and 0- ≈ 10 wt% CaO) iron silicate slags has been measured at 1,300°C. In order to avoid contamination and the effects of further elements in the slag, the measurements were carried out at silica saturation. The solubility of chromium was a function of oxygen partial pressure. At high oxygen partial pressures P O2  ≈ 10 −5  atm, the solubility was about 0.15 wt% (Cr) and it increased to about 0.3 wt% (Cr) in reducing conditions of p O2  ≈ 10 −10  atm. Alumina and lime seemed to increase the solubility slightly.

AlkuperäiskieliEnglanti
JulkaisuMineral Processing and Extractive Metallurgy Review
DOI - pysyväislinkit
TilaJulkaistu - 1 tammikuuta 2019
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Sormenjälki

Sukella tutkimusaiheisiin 'Slag–Copper Equilibria of Selected Trace Elements in Black Copper Smelting. Part I. Properties of the Slag and Chromium Solubility'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä