Self-assembled La0.7Sr0.3Fe0.9Ni0.1O3-δ-Ce0.8Sm0.2O2-δ composite cathode with a three-dimensional ordered macroporous structure for protonic ceramic fuel cells

Xin Zhao, Jian Zhang, Xuanlin Lu, Wen Liu, Jiaxuan Chen, Yicheng Zhao*, Yongdan Li

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

1 Sitaatiot (Scopus)

Abstrakti

Self-assembled La0.7Sr0.3Fe0.9Ni0.1O3-δ-Ce0.8Sm0.2O1.9-δ (LSFN-SDC) composite cathode with a three-dimensionally ordered macroporous (3DOM) structure is synthesized using poly(methyl methacrylate) as the template for protonic ceramic fuel cells. The LSFN and SDC phases both distribute uniformly in the cathode. The SDC phase reduces the thickness of the walls of the 3DOM structure and thus hinders the bulk conduction of electrons. SDC also decreases the specific surface area and the surface oxygen reactivity of the cathode, leading to the suppression of the adsorption and dissociation of O2. However, the SDC phase provides the conduction pathway for oxygen ions and enlarges three phase boundary consequently, which facilitates the charge transfer steps. The thickness of the walls and the specific surface area of the composite cathode are both increased with the rise of the concentration of the nitrate precursor solution, resulting in the acceleration of the cathode process. Nevertheless, an excessive precursor concentration leads to the destroy of the 3DOM structure. The 3DOM composite cathode exhibits the lowest Rp of 0.039 Ω cm2, and a single cell with that cathode shows maximum power density of 1484 mW cm−2 at 700 °C. The cell exhibits a short-term stability of 120 h at 700 °C without noticeable degradation.

AlkuperäiskieliEnglanti
Artikkeli116582
JulkaisuSolid State Ionics
Vuosikerta412
Varhainen verkossa julkaisun päivämäärä10 toukok. 2024
DOI - pysyväislinkit
TilaJulkaistu - syysk. 2024
OKM-julkaisutyyppiA1 Alkuperäisartikkeli tieteellisessä aikakauslehdessä

Sormenjälki

Sukella tutkimusaiheisiin 'Self-assembled La0.7Sr0.3Fe0.9Ni0.1O3-δ-Ce0.8Sm0.2O2-δ composite cathode with a three-dimensional ordered macroporous structure for protonic ceramic fuel cells'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä