Role of impurity copper in Li-ion battery recycling to LiCoO2 cathode materials

Tutkimustuotos: Lehtiartikkeli

Tutkijat

Organisaatiot

Kuvaus

Copper is a dominating impurity in Co-rich Li(Co,Ni,Mn)O2 battery waste fractions and may exist in similar quantities (e.g. 6 wt%) as Li, Ni and Mn. This paper investigates the behavior of copper from waste batteries up to recycled active materials and the findings highlight that copper contamination is not necessarily detrimental for the active materials in trace amounts, but can rather increase the discharge capacity at high rates. Firstly, industrially crushed battery waste was treated hydrometallurgically to produce Li2CO3 and CoSO4·2H2O precipitates for re-use, before being calcined to prepare fresh LiCoO2 materials. Results suggest that during the hydrometallurgical recycling process, Cu is likely to co-extract along the Co; in the current work both high and low Cu-contaminated CoSO4·2H2O precipitates were obtained and in the former case, formation of CuO as a secondary phase occurred upon calcination. The presence of Cu contamination induced up to ca. 35 mAh/g decrease in the specific capacity, compared to pure LiCoO2. However, a low level of Cu inclusion was found to be advantageous at high discharge rates (4.0C and 5.0C) resulting in a doubling of the capacity (110–120 mAh/g) when compared with pure LiCoO2 (40–60 mAh/g).

Yksityiskohdat

AlkuperäiskieliEnglanti
Artikkeli227630
JulkaisuJournal of Power Sources
Vuosikerta450
TilaJulkaistu - 29 helmikuuta 2020
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Lataa tilasto

Ei tietoja saatavilla

ID: 39994142