Phase equilibrium study of the CaO–SiO2–CrOx system at 1600°C in reducing atmospheres

Min Chen, Pekka Taskinen, Dmitry Sukhomlinov, Daniel Lindberg*, Radoslaw Michallik, Ari Jokilaakso

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

16 Lataukset (Pure)

Abstrakti

Phase equilibria in the CaO–SiO2–CrOx system were experimentally investigated at 1600°C and pO2 of 10−10 to 10−11 atm using the high-temperature isothermal equilibration/drop quenching/electron probe X-ray microanalysis technique. The constrained isothermal sections of the CaO–SiO2–CrOx system were constructed at 1600°C and pO2 of 10−10 to 10−11 atm based on the experimental results. The primary phase fields including cristobalite (SiO2), larnite (Ca2SiO4), (Ca,Cr)Cr2O4, and corundum (Cr2O3) were determined. Simulations by thermodynamic software MTDATA, FactSage, and Thermo-Calc were compared with the present experimental results.

AlkuperäiskieliEnglanti
Sivut3436-3450
Sivumäärä15
JulkaisuJournal of the American Ceramic Society
Vuosikerta107
Numero5
Varhainen verkossa julkaisun päivämäärä22 jouluk. 2023
DOI - pysyväislinkit
TilaJulkaistu - toukok. 2024
OKM-julkaisutyyppiA1 Alkuperäisartikkeli tieteellisessä aikakauslehdessä

Sormenjälki

Sukella tutkimusaiheisiin 'Phase equilibrium study of the CaO–SiO2–CrOx system at 1600°C in reducing atmospheres'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä