Phase equilibria of the CaO–SiO2–TiO2–Al2O3–MgO system in air at 1250–1400 °C

Min Chen, Junjie Shi*, Pekka Taskinen, Ari Jokilaakso

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

2 Sitaatiot (Scopus)

Abstrakti

The equilibrium phase relations of the CaO–SiO2–TiO2–Al2O3–MgO system were investigated experimentally in air at 1250–1400 °C using a high-temperature equilibration/quenching technique, followed by direct phase analysis by scanning electron microscopy equipped with X-ray energy dispersive spectroscopy. The equilibrium solid phases of silica, rutile, and pseudobrookite solid solution were found to coexist with the liquid phase. The 1300–1400 °C isothermal sections were constructed based on the experimentally measured liquid compositions. The experimental results were compared with simulations using MTDATA and FactSage thermodynamic software and their databases. This study provides guidelines for the selective crystallization of pseudobrookite from titania-bearing slag.
AlkuperäiskieliEnglanti
Sivut27702-27710
Sivumäärä9
JulkaisuCeramics International
Vuosikerta46
Numero17
Varhainen verkossa julkaisun päivämäärä31 heinäkuuta 2020
DOI - pysyväislinkit
TilaJulkaistu - 1 joulukuuta 2020
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Sormenjälki

Sukella tutkimusaiheisiin 'Phase equilibria of the CaO–SiO2–TiO2–Al2O3–MgO system in air at 1250–1400 °C'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä