Phase equilibria in the BaO-SiO2-Al2O3 ternary system at 1500°C

Rui Zhang*, Pekka Taskinen

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: Artikkeli kirjassa/konferenssijulkaisussaConference contributionScientificvertaisarvioitu

Abstrakti

Phase equilibria of the BaO-SiO2-Al2O3 ternary system was experimentally investigated using a quenching technique and analyzed by Scanning Electron Microscopy (SEM) equipped with Energy Dispersive Analysis (EDS) and X-ray Powder Diffraction (XRD). A ternary compound was confirmed in the present work. The liquid's composition in equilibrium with the ternary compound at 1500 °C were quantified. The isothermal sections of the BaO-SiO2-Al2O3 ternary system at 1400 °C, 1500 °C, 1600 °C, and 1700 °C were calculated. Based on the data acquired, the isothermal section at 1500 °C was constructed.

AlkuperäiskieliEnglanti
OtsikkoHigh-Performance Ceramics IX
KustantajaTrans Tech Publications Ltd.
Sivut565-571
Sivumäärä7
Vuosikerta697
ISBN (painettu)9783035710656
DOI - pysyväislinkit
TilaJulkaistu - 2016
OKM-julkaisutyyppiA4 Artikkeli konferenssijulkaisuussa
TapahtumaChina International Conference on High-Performance Ceramics - Guilin, Kiina
Kesto: 4 marrask. 20157 marrask. 2015
Konferenssinumero: 9

Julkaisusarja

NimiKey Engineering Materials
Vuosikerta697
ISSN (painettu)10139826

Conference

ConferenceChina International Conference on High-Performance Ceramics
LyhennettäCICC
Maa/AlueKiina
KaupunkiGuilin
Ajanjakso04/11/201507/11/2015

Sormenjälki

Sukella tutkimusaiheisiin 'Phase equilibria in the BaO-SiO2-Al2O3 ternary system at 1500°C'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä