Perpendicular magnetic anisotropy in Bi-substituted yttrium iron garnet films

Sreeveni Das, Rhodri Mansell*, Lukáš Flajšman, Lide Yao, Sebastiaan van Dijken*

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

26 Lataukset (Pure)

Abstrakti

Magnetic garnet thin films exhibiting perpendicular magnetic anisotropy (PMA) and ultra-low damping have recently been explored for applications in magnonics and spintronics. Here, we present a systematic study of PMA and magnetic damping in bismuth-substituted yttrium iron garnet (Bi-YIG) films grown on sGGG (111) substrates by pulsed laser deposition. Films with thicknesses ranging from 5 to 160 nm are investigated. Structural characterization using x-ray diffraction and reciprocal space mapping demonstrates the pseudomorphic growth of the films. The films exhibit perpendicular magnetic anisotropy up to 160 nm thickness, with the zero-magnetic field state changing from fully saturated for low thicknesses to a dense magnetic stripe pattern for thicker films. The films show a ferromagnetic resonance (FMR) linewidth of 100-200 MHz with a Gilbert damping constant of the order of 4 × 10 − 3 . The broad FMR linewidth is caused by inhomogeneities of magnetic properties on micrometer length scales.

AlkuperäiskieliEnglanti
Artikkeli243902
Sivut1-7
Sivumäärä7
JulkaisuJournal of Applied Physics
Vuosikerta134
Numero24
DOI - pysyväislinkit
TilaJulkaistu - 26 jouluk. 2023
OKM-julkaisutyyppiA1 Alkuperäisartikkeli tieteellisessä aikakauslehdessä

Sormenjälki

Sukella tutkimusaiheisiin 'Perpendicular magnetic anisotropy in Bi-substituted yttrium iron garnet films'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä