Perpendicular exchange bias in nickel/antiferromagnetic bilayers

Tutkimustuotos: Lehtiartikkelivertaisarvioitu

Tutkijat

Organisaatiot

  • Trinity College Dublin

Kuvaus

A study of exchange-biased Ni films with perpendicular magnetic anisotropy is presented. Polar magneto-optic Kerr effect measurements on unbiased Si(0 0 1)/Cu/Ni/Cu films reveal high out-of-plane remanence and a loop squareness close to unity. After deposition of an antiferromagnetic layer on top of the Ni film the magnetization direction remains perpendicular to the film plane and for FeMn, IrMn, and NiMn a shift in the hysteresis loop is observed. The perpendicular exchange bias is largest for FeMn, considerably smaller for IrMn and NiMn, and zero for PtMn. All antiferromagnetic films exhibit a (0 0 1) oriented texture.

Yksityiskohdat

AlkuperäiskieliEnglanti
Sivut1290-1293
Sivumäärä4
JulkaisuJournal of Magnetism and Magnetic Materials
Vuosikerta290-291
NumeroPart 2
TilaJulkaistu - huhtikuuta 2005
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

ID: 5396664