Optically controlled large-coercivity room-temperature thin-film magnets

Anish Philip, Yifan Zhou, Girish C. Tewari, Sebastiaan van Dijken, Maarit Karppinen*

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

1 Sitaatiot (Scopus)
6 Lataukset (Pure)

Abstrakti

Photo-controlled room-temperature hard magnets could open new horizons for high-density information storage. For this, the material should be fabricated as device-integrable (conformal, stretchable, transparent,etc.) thin films and preferably from readily available and innocuous chemical constituents. Here we report a viable material candidate to address all these criteria. The material basis is the ferrimagnetic ε-Fe 2O 3polymorph of trivalent iron oxide with an exceptionally high room-temperature magnetic coercivity. To bring the photo-controllability, azobenzene moieties withtrans-cisisomerization tendency are embedded into this matrix as regular monomolecular layers. The strongly emerging atomic/molecular layer deposition (ALD/MLD) technique offers us a scientifically elegant yet industrially feasible tool to fabricate these superlattice thin films with nanoscale precision. We demonstrate reversible changes in both coercivity and magnetization values with alternating irradiations of the films with UV and visible light. Interestingly, the azobenzene layers not only add this switching functionality but also enhance the overall magnetic performance of the ε-Fe 2O 3matrix.

AlkuperäiskieliEnglanti
Sivut294-300
Sivumäärä7
JulkaisuJournal of Materials Chemistry C
Vuosikerta10
Numero1
Varhainen verkossa julkaisun päivämäärä25 marraskuuta 2021
DOI - pysyväislinkit
TilaJulkaistu - 23 joulukuuta 2021
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Sormenjälki

Sukella tutkimusaiheisiin 'Optically controlled large-coercivity room-temperature thin-film magnets'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä