Nanofibrillated cellulose/carboxymethyl cellulose composite with improved wet strength

Nikolaos Pahimanolis, Arto Salminen, Paavo A. Penttilä, Juuso T. Korhonen, Leena-Sisko Johansson, Janne Ruokolainen, Ritva Serimaa, Jukka Seppälä

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

70 Sitaatiot (Scopus)

Abstrakti

In this paper, nanofibrillated cellulose/carboxymethyl cellulose (CMC) composite films were prepared using tape casting. The obtained transparent films showed shear induced partial alignment of fibrils along the casting direction, resulting in birefringence in cross polarized light. The carboxyl groups of CMC could be further utilized to create ionic crosslinking by treatment with glycidyl trimethyl ammonium chloride (GTMA). The GTMA treated composite films had improved mechanical properties both in wet and dry state. The chemical composition and morphologies of composites were analyzed with X-ray photoelectron spectroscopy, elemental analysis, scanning electron microscopy and wide-angle X-ray scattering.
AlkuperäiskieliEnglanti
Sivut1459-1468
Sivumäärä10
JulkaisuCellulose
Vuosikerta20
Numero3
DOI - pysyväislinkit
TilaJulkaistu - 2013
OKM-julkaisutyyppiA1 Alkuperäisartikkeli tieteellisessä aikakauslehdessä

Sormenjälki

Sukella tutkimusaiheisiin 'Nanofibrillated cellulose/carboxymethyl cellulose composite with improved wet strength'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä