Abstrakti
The influence of the structural state on deformation mechanisms under large strains was investigated in a Cu – 2 wt.% Be alloy. Torque evolutions during straining exhibit serrations typical of structural relaxations in the precipitation-hardened alloy, but not in the solid solution state. Microstructure characterization revealed that homogeneous deformation of the solid solution led to strong grain size reduction (20 nm), while localization occurred in the precipitated state with numerous shear bands. The role of CuBe precipitates on hindering dislocation glide and the resulting shear localization under large strain is discussed.
Alkuperäiskieli | Englanti |
---|---|
Artikkeli | 141760 |
Sivumäärä | 6 |
Julkaisu | Materials Science and Engineering A |
Vuosikerta | 823 |
DOI - pysyväislinkit | |
Tila | Julkaistu - 17 elok. 2021 |
OKM-julkaisutyyppi | A1 Alkuperäisartikkeli tieteellisessä aikakauslehdessä |
Sormenjälki
Sukella tutkimusaiheisiin 'Mechanism of large strain accommodation assisted by shear localization in a precipitation-hardened Cu–Be alloy'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.Projektit
- 1 Päättynyt
-
Fluctuations in Fracture --- Fluktuaatiot murtumisessa
Alava, M. (Vastuullinen tutkija), Lomakin, I. (Projektin jäsen), Ranta, R. (Projektin jäsen), Savolainen, J. (Projektin jäsen), Koivisto, J. (Projektin jäsen), Salmenjoki, H. (Projektin jäsen) & Viitanen, L. (Projektin jäsen)
01/09/2018 → 31/08/2022
Projekti: Academy of Finland: Other research funding
Laitteet
-
-
OtaNano Nanomikroskopiakeskus
Seitsonen, J. (Manager) & Rissanen, A. (Other)
OtaNanoLaitteistot/tilat: Facility