Mechanical properties and applications of recycled polycarbonate particle material extrusion-based additive manufacturing

Tutkimustuotos: Lehtiartikkelivertaisarvioitu

Tutkijat

  • Matthew J. Reich
  • Aubrey L. Woern
  • Nagendra G. Tanikella
  • Joshua Pearce

Organisaatiot

  • Michigan Technological University

Kuvaus

Past work has shown that particle material extrusion (fused particle fabrication (FPF)/fused granular fabrication (FGF)) has the potential for increasing the use of recycled polymers in 3D printing. This study extends this potential to high-performance (high-mechanical-strength and heat-resistant) polymers using polycarbonate (PC). Recycled PC regrind of approximately 25 mm2 was 3D printed with an open-source Gigabot X and analyzed. A temperature and nozzle velocity matrix was used to find useful printing parameters, and a print test was used to maximize the output for a two-temperature stage extruder for PC. ASTM type 4 tensile test geometries as well as ASTM-approved compression tests were used to determine the mechanical properties of PC and were compared with filament printing and the bulk virgin material. The results showed the tensile strength of parts manufactured from the recycled PC particles (64.9 MPa) were comparable to that of the commercial filament printed on desktop (62.2 MPa) and large-format (66.3 MPa) 3D printers. Three case study applications were investigated: (i) using PC as a rapid molding technology for lower melting point thermoplastics, (ii) printed parts for high temperature applications, and (iii) printed parts for high-strength applications. The results show that recycled PC particle-based 3D printing can produce high-strength and heat-resistant products at low costs.

Yksityiskohdat

AlkuperäiskieliEnglanti
Artikkeli1642
Sivumäärä18
JulkaisuMaterials
Vuosikerta12
Numero10
TilaJulkaistu - 1 toukokuuta 2019
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Lataa tilasto

Ei tietoja saatavilla

ID: 34936866