Long life spectrum fatigue of carbon and stainless steel welds

Tutkimustuotos: Lehtiartikkelivertaisarvioitu

Tutkijat

Organisaatiot

  • VTT Technical Research Centre of Finland

Kuvaus

Fatigue tests of non-load carrying carbon and stainless steel fillet welds have been performed using spectrum loading typical for rail vehicles. The proportion of spectrum cycles exceeding the constant amplitude fatigue limit ranged between 0.86% and 100% and cycles to failure ranged from 4.2 x 10(5) to 2.1 x 10(7). For the longest tests, the majority of fatigue damage was contributed by cycles with stress ranges less than the constant amplitude fatigue limit. For the carbon steel welds a significant portion of fatigue damage was produced by cycles with stress ranges less than 50% of the fatigue limit but only a small fraction of damage was produced by cycles of this size for the stainless steel welds. The carbon steel welds had slightly better fatigue strength at lives less than 10(7) cycles but results suggest that stainless steels may have superior long-life variable amplitude fatigue strength when a greater portion of life is spent in the early stages of crack nucleation and growth.

Yksityiskohdat

AlkuperäiskieliEnglanti
Sivut739-753
Sivumäärä15
JulkaisuFatigue and Fracture of Engineering Materials and Structures
Vuosikerta19
Numero6
TilaJulkaistu - 1996
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

ID: 3207290