Large-area highly crystalline WSe2 atomic layers for ultrafast pulsed lasers

Tutkimustuotos: Lehtiartikkelivertaisarvioitu

Tutkijat

  • Y. I.N. Jinde
  • L. I. Jiarong
  • Hao Chen
  • Jintao Wang
  • Y. A.N. Peiguang
  • L. I.U. Mengli
  • L. I.U. Wenjun
  • L. U. Wei
  • X. U. Zihan
  • Wenfei Zhang
  • Jinzhang Wang
  • Zhipei Sun

  • Shuangchen Ruan

Organisaatiot

  • Shenzhen University
  • Beijing University of Posts and Telecommunications
  • Hong Kong Polytechnic University
  • Shenzen 6Carbon Technology

Kuvaus

Large-area and highly crystalline transition metal dichalcogenides (TMDs) films possess superior saturable absorption compared to the TMDs nanosheet counterparts, which make them more suitable as excellent saturable absorbers (SA) for ultrafast laser technology. Thus far, the nonlinear optical properties of large-scale WSe2 and its applications in ultrafast photonics have not yet been fully investigated. In this work, the saturable absorption of chemical vapor deposition (CVD) grown WSe2 films with large-scale and high quality are studied and the use of WSe2 films as a broadband SA for passively mode-locked fiber lasers at both 1.5 and 2 μm ranges is demonstrated. To enhance the light-material interaction, large-area WSe2 film is tightly transferred onto the side wall of a microfiber to form a hybrid structure, which realizes strong evanescent wave interaction between light and WSe2 film. The integrated microfiber-WSe2 device shows a large modulation depth of 54.5%. Using the large-area WSe2 as a mode-locker, stable soliton mode-locked pulse generation is achieved and the pulse durations of 477 fs (at 1.5 μm) and 1.18 ps (at 2.0 μm) are demonstrated, which suggests that the large-area and highly crystalline WSe2 films afford an excellent broadband SA for ultrafast photonic applications.

Yksityiskohdat

AlkuperäiskieliEnglanti
Sivut30020-30031
Sivumäärä12
JulkaisuOptics Express
Vuosikerta25
Numero24
TilaJulkaistu - 27 marraskuuta 2017
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Lataa tilasto

Ei tietoja saatavilla

ID: 16605163