Issledovanie rezhimov prokalki termoantracita dlya proizvodstva nepreryvnyh samoobzhygayuschihsja elektrodov rudovosstanovitelnyh pechei

S.V. Kutuzov, V.V. Derkach, M.I. Gasik, A.P. Gorobets, Michael Gasik

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

Abstrakti

The process of graphitization of anthracite as a carbon component of self-baking electrodes is considered. Experimental studies of the physical properties of thermoanthracite by thermogravimetry and IR spectroscopy in the temperature range 400…1400 °C were performed. Regression models of the relationship between the structure of thermoanthracite, strength, thermal conductivity and resistivity and the temperature regime of anthracite calcination were created. Ref. 9, Tabl. 4, Fig. 7.
Keywords: thermoanthracite; self-baking electrodes; thermophysical characteristics; dynamic thermogravimetry; IR spectroscopy; crystallites; density; electrical conductivity; phase composition
Julkaisun otsikon käännösResearch of the influence of thermoanthracite calcination modes for the production of continuous self-baking electrodes for ore-reduction furnaces
AlkuperäiskieliVenäjä
Sivut43-45
JulkaisuAdvances in Electrometallurgy
Numero1
DOI - pysyväislinkit
TilaJulkaistu - 2020
OKM-julkaisutyyppiA1 Alkuperäisartikkeli tieteellisessä aikakauslehdessä