Influence of temperature of thermal treatment on surface densification of spruce

Mirko Kariz*, Manja Kitek Kuzman, Milan Sernek, Mark Hughes, Lauri Rautkari, Frederick A. Kamke, Andreja Kutnar

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

29 Sitaatiot (Scopus)

Abstrakti

Spruce (Picea abies L. Karst) wood lamellae, thermally treated at 170, 190, 210 and 230 °C were surface densified by compression at a temperature of 150 °C to three degrees of compression. Immediate springback, set recovery, mechanical properties in 3-point flexure, Brinell hardness and density profiles measurements were used to determine the effect of thermal treatment on the properties of surface densified wood. The highest immediate springback occurred in wood specimens thermally treated at the highest temperature (230 °C) and decreased with decreasing thermal treatment temperature. The untreated samples had the highest set recovery, which decreased with the temperature of thermal treatment. The surface densification increased hardness and bending strength. The highest increase was in the case of untreated wood and decreased with the temperature of thermal treatment. The modulus of elasticity (MOE) and modulus of rupture (MOR) of surface densified wood decreased with increasing thermal treatment temperature. The trend was similar for specimens which were thermally treated but not surface densified. Surface densification increased the density of the specimens in the first few millimetres below the surface. The highest density was achieved in untreated specimens and the lowest in specimens thermally treated at the highest temperature.

AlkuperäiskieliEnglanti
Sivut113-123
Sivumäärä11
JulkaisuEuropean Journal of Wood and Wood Products
Vuosikerta75
Numero1
Varhainen verkossa julkaisun päivämäärä12 toukokuuta 2016
DOI - pysyväislinkit
TilaJulkaistu - tammikuuta 2017
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Sormenjälki

Sukella tutkimusaiheisiin 'Influence of temperature of thermal treatment on surface densification of spruce'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä