Influence of CO and H2 adsorption on the spin reorientation transition in Ni/Cu(001)

S. van Dijken, R. Vollmer, B. Poelsema, J. Kirschner

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

55 Sitaatiot (Scopus)

Abstrakti

A strong reduction of the critical thickness of the spin reorientation transition in Ni/Cu(001) has been observed when covered with CO or H2. For uncovered Ni films a critical thickness of 10.5 ML has been found at T = 300 K. The critical thickness is reduced by about 3 and 4 ML after adsorption of 0.5 ML CO and H2, respectively. The observed shift in the spin reorientation transition implies a reduction of the negative surface anisotropy energy by about 50% in both cases.

AlkuperäiskieliEnglanti
Sivut316-328
Sivumäärä13
JulkaisuJournal of Magnetism and Magnetic Materials
Vuosikerta210
Numero1-3
DOI - pysyväislinkit
TilaJulkaistu - helmikuuta 2000
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Sormenjälki

Sukella tutkimusaiheisiin 'Influence of CO and H<sub>2</sub> adsorption on the spin reorientation transition in Ni/Cu(001)'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä