High cycle variable amplitude fatigue of a nodular cast iron

GB Marquis*, BR Rabb, P Karjalainen-Roikonen

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: Artikkeli kirjassa/konferenssijulkaisussaConference contributionScientificvertaisarvioitu

Abstrakti

This paper provides a brief summary of life prediction methods for variable amplitude fatigue. Special attention is given to cracks propagating from nominally defect free components in the high cycle regime where a significant portion of the fatigue damage can be attributed to cycles with amplitude less than the fatigue limit observed under constant amplitude loading. Constant and variable amplitude fatigue data for a nodular cast iron are presented. An effective stress method for variable amplitude loaded similar to the Topper model is developed. Most model parameters are derived from constant amplitude S-N curves and the Haigh diagram, but two sets of long life variable amplitude tests are needed to derive the variable amplitude interaction parameters.

AlkuperäiskieliEnglanti
OtsikkoFatigue Testing and Analysis Under Variable Amplitude Loading Conditions
ToimittajatPC McKeighan, N Ranganathan
KustantajaAMERICAN SOCIETY FOR TESTING AND MATERIALS
Sivut215-231
Sivumäärä17
ISBN (painettu)0-8031-3479-7
TilaJulkaistu - 2005
OKM-julkaisutyyppiA4 Artikkeli konferenssijulkaisuussa
TapahtumaSymposium on Fatigue Testing and Analysis Under Variable Amplitude Loading Conditions - Tours, Ranska
Kesto: 29 toukokuuta 200231 toukokuuta 2002

Julkaisusarja

NimiAMERICAN SOCIETY FOR TESTING AND MATERIALS SPECIAL TECHNICAL PUBLICATION
KustantajaAMERICAN SOCIETY TESTING AND MATERIALS
Vuosikerta1439
ISSN (painettu)1040-1695

Conference

ConferenceSymposium on Fatigue Testing and Analysis Under Variable Amplitude Loading Conditions
MaaRanska
KaupunkiTours
Ajanjakso29/05/200231/05/2002

Siteeraa tätä