Grain refinement processes for superplastic forming of AISI 304 and 304L austenitic stainless steels

Yuriy Yagodzinskyy, Joe Pimenoff, O. Tarasenko, Jyrki Romu, Pertti Nenonen, Hannu Hänninen

    Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

    15 Sitaatiot (Scopus)

    Abstrakti

    Elongation to fracture values higher than 300% were obtained for cold rolled AISI 304 type steel grades in hot tensile tests. The effects of heating rate and carbon content on the elongation of the steels studied are discussed based on internal friction measurements and TEM observations. A slow heating rate to the test temperature and high carbon content of the steel led to a fine and equiaxial grain structure of the steels.

    AlkuperäiskieliEnglanti
    Sivut925-929
    Sivumäärä5
    JulkaisuMaterials Science and Technology
    Vuosikerta20
    Numero7
    DOI - pysyväislinkit
    TilaJulkaistu - heinäk. 2004
    OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

    Sormenjälki

    Sukella tutkimusaiheisiin 'Grain refinement processes for superplastic forming of AISI 304 and 304L austenitic stainless steels'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

    Siteeraa tätä