Fracture properties of zinc coating layers in a galvannealed steel and an electrolytically galvanized steel

Jinshan He, Junhe Lian*, Anke Aretz, Napat Vajragupta, Ude Hangen, Frank Goodwin, Sebastian Münstermann

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

1 Sitaatiot (Scopus)

Abstrakti

The zinc coating layer fracture properties of a galvannealed steel and an electrolytically galvanized steel are analyzed by conducting the in-situ bending test with newly designed samples. It is found that the fracture develops much earlier in the coating layers of the galvannealed steel than that of the electrolytically galvanized steel. Using transmission electron microscope and energy dispersive X-ray spectroscopy, the intermetallic phases of the coating layers are characterized and it is found that the early crack initiation in a galvannealed steel is mainly triggered in the gamma phase. Combining with nanoindentation tests and corresponding simulation, the deformability of intermetallic phases are analyzed to explain the failure behavior of coating layers in the two steels.

AlkuperäiskieliEnglanti
Sivut320-325
Sivumäärä6
JulkaisuMATERIALS SCIENCE AND ENGINEERING A: STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
Vuosikerta732
DOI - pysyväislinkit
TilaJulkaistu - 8 elokuuta 2018
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Sormenjälki Sukella tutkimusaiheisiin 'Fracture properties of zinc coating layers in a galvannealed steel and an electrolytically galvanized steel'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

  • Siteeraa tätä