Formation of ruthenium cluster on nanocrystalline tungsten trioxide

Y. Fujioka*, J. Frantti, R.M. Nieminen, A. M. Asiri

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

7 Sitaatiot (Scopus)

Abstrakti

Ruthenium (Ru)-modified (up to 1 wt %) tungsten trioxide (WO3) samples were synthesized and characterized by X-ray diffraction, X-ray photoelectron spectroscopy (XPS), scanning and transmission electron microscopy, and Raman spectroscopy. Ru was found to form hexagonal clusters on {111} planes of the underlying WO3 crystals with similar arrangement as is found in metal Ru. XPS revealed that the valence state of ruthenium corresponds to the oxidized state. Results indicate that bonding between Ru and oxygen of the crystal surfaces is a key factor for the cluster formation. No evidence for a crystalline ruthenium oxide or metal phase formation was found instead Ru atoms were bonded on oxygen on the WO3 {111} planes.

AlkuperäiskieliEnglanti
Sivut7506-7510
Sivumäärä5
JulkaisuJournal of Physical Chemistry C
Vuosikerta117
Numero15
DOI - pysyväislinkit
TilaJulkaistu - 18 huhtikuuta 2013
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Sormenjälki Sukella tutkimusaiheisiin 'Formation of ruthenium cluster on nanocrystalline tungsten trioxide'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

  • Laitteet

    OtaNano

    Anna Rissanen (Manager)

    Aalto-yliopisto

    Laitteistot/tilat: Facility

  • Siteeraa tätä