Film Conformality and Extracted Recombination Probabilities of O Atoms during Plasma-Assisted Atomic Layer Deposition of SiO2, TiO2, Al2O3, and HfO2

Tutkimustuotos: Lehtiartikkeli

Tutkijat

  • Karsten Arts
  • Mikko Utriainen
  • Riikka Puurunen

  • Wilhelmus M.M. Kessels
  • Harm C.M. Knoops

Organisaatiot

  • Eindhoven University of Technology
  • VTT Technical Research Centre of Finland
  • Oxford Instruments Group Plc

Kuvaus

Surface recombination of plasma radicals is generally considered to limit film conformality during plasma-assisted atomic layer deposition (ALD). Here, we experimentally studied film penetration into high-aspect-ratio structures and demonstrated that it can give direct information on the recombination probability r of plasma radicals on the growth surface. This is shown for recombination of oxygen (O) atoms on SiO2, TiO2, Al2O3, and HfO2 where a strong material dependence has been observed. Using extended plasma exposures, films of SiO2 and TiO2 penetrated extremely deep up to an aspect ratio (AR) of â900, and similar surface recombination probabilities of r = (6 ± 2) × 10-5 and (7 ± 4) × 10-5 were determined for these processes. Growth of Al2O3 and HfO2 was conformal up to depths corresponding to ARs of â80 and â40, with r estimated at (1-10) × 10-3 and (0.1-10) × 10-2, respectively. Such quantitative insight into surface recombination, as provided by our method, is essential for modeling radical-surface interaction and understanding for which materials and conditions conformal film growth is feasible by plasma-assisted ALD.

Yksityiskohdat

AlkuperäiskieliEnglanti
Sivut27030-27035
Sivumäärä6
JulkaisuJournal of Physical Chemistry C
Vuosikerta123
Numero44
TilaJulkaistu - 7 marraskuuta 2019