Ferroelectric parallel-plate capacitors with copper electrodes for high-frequency applications

Tommi Riekkinen*, Tomi Mattila, Sebastiaan van Dijken, A. Lüker, Qi Zhang, Paul B. Kirby, Ana M. Sánchez

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

10 Sitaatiot (Scopus)

Abstrakti

Tunable capacitors with a Cu Pbx Sr1-x Ti O3 Cu parallel-plate structure have been fabricated using a layer transfer method. The use of a Cu bottom electrode results in a giant electrode Q-factor×capacitor area product of Qelec A=3.79× 105 μ m2 at 1 GHz. The dielectric constant at room temperature is 420 and the tunability amounts to 73% near a breakdown voltage of 35 V. The major advantages of the layer transfer method include low electrode losses, the freedom to select an auxiliary substrate and seed layer for ferroelectric film growth irrespective of their high-frequency properties, and the possibility to utilize a large variety of device substrates as they no longer act as template for film growth.

AlkuperäiskieliEnglanti
Artikkeli252902
Sivumäärä3
JulkaisuApplied Physics Letters
Vuosikerta91
Numero25
DOI - pysyväislinkit
TilaJulkaistu - 2007
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Sormenjälki

Sukella tutkimusaiheisiin 'Ferroelectric parallel-plate capacitors with copper electrodes for high-frequency applications'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä