Fatigue strength of high-strength steel after shipyard production process of plasma cutting, grinding, and sandblasting

Tutkimustuotos: Lehtiartikkelivertaisarvioitu

Tutkijat

Organisaatiot

  • TUHH
  • Meyer Turku Oy

Kuvaus

This paper investigates experimentally the fatigue strength of high-strength steel, which has undergone the normal shipyard production process of plasma cutting, grinding, and sandblasting. The study includes steels with the yield strength of 355 and 690 MPa. The tested specimens are of dog-bone shape and represent the large-scale situation of a cruise ship balcony opening corner, loaded in shear or tension. The influence of surface roughness, internal inclusions, hardness, and residual stress on the fatigue strength are studied and discussed. Compared to the design curve as well as to the untreated surfaces, the results show significantly improved fatigue strength under constant amplitude loading at a load ratio of R = 0.1. However, very flat or even rising slope of the S-N curve indicates variations in the material and surface quality as well as in the residual stress. Surprisingly, internal defects even up to 100 μm in size did not decrease the fatigue strength.

Yksityiskohdat

AlkuperäiskieliEnglanti
Sivut1273-1284
Sivumäärä12
JulkaisuWelding in the World
Vuosikerta62
Numero6
TilaJulkaistu - marraskuuta 2018
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

ID: 31331879