Fatigue life and surface integrity measurements of EN S355J2 steel used in hydraulic components

Jiří Čuban*, Olof Calonius, Matti Pietola, Jan Jersák

*Tämän työn vastaava kirjoittaja

    Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

    8 Sitaatiot (Scopus)

    Abstrakti

    This article is aimed at studying the impact of surface integrity - surface roughness, hardness and residual stress - on fatigue performance of EN S355J2 steel. The test specimens were manufactured by turning. A longer fatigue life for the machined components can be obtained by applying such cutting conditions as a low feed rate. The fatigue limit of the specimen with the surface roughness Ra 1,6 Dm is approximately 7 % higher than that of the specimen with Ra 3,2 Dm. From the residual stress results it can be seen that the cutting conditions used for producing surface finish Ra 1,6 Dm will introduce mainly compressive residual stress whereas the cutting conditions used for producing surface finish Ra 3,2 Dm will introduce tensile residual stress. The measurements were carried out at Aalto University at the Departments of Engineering Design and Production and Material Science and Engineering in Espoo. The main purpose of the study is to find proper surface finishing techniques and fatigue improvements for hydraulic components.

    AlkuperäiskieliEnglanti
    Sivut5-11
    Sivumäärä7
    JulkaisuManufacturing Technology
    Vuosikerta11
    TilaJulkaistu - joulukuuta 2011
    OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

    Sormenjälki Sukella tutkimusaiheisiin 'Fatigue life and surface integrity measurements of EN S355J2 steel used in hydraulic components'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

    Siteeraa tätä