@techreport{8b8d11633a3648ed8f17334d1f3c33bd,
title = "Environment-assisted Cracking and Hot Cracking Susceptibility of Nickel-base Alloy Weld Metals",
keywords = "differential scanning calorimetry, dynamic strain aging, electron microscopy, environment-assisted cracking, hot cracking, nickel-base alloys, residual stress, weld metal, differential scanning calorimetry, dynamic strain aging, electron microscopy, environment-assisted cracking, hot cracking, nickel-base alloys, residual stress, weld metal, differential scanning calorimetry, dynamic strain aging, electron microscopy, environment-assisted cracking, hot cracking, nickel-base alloys, residual stress, weld metal",
author = "Hannu H{\"a}nninen and Anssi Brederholm and Tapio Saukkonen and Mykola Ivanchenko and Aki Toivonen and Wade Karlsen and Ulla Ehrnsten and Pertti Aaltonen",
note = "VK: T20309",
year = "2011",
language = "English",
isbn = "978-951-38-7709-5",
series = "VTT Research Notes",
publisher = "VTT",
number = "2582",
pages = "153",
type = "WorkingPaper",
institution = "VTT",
}