Electromagnetic and Thermoelectric Characteristics of Na xCoO2 of Precisely Controlled Na Nonstoichiometry

Teruki Motohashi*, Maarit Karppinen, Hisao Yamauchi

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliConference articleScientificvertaisarvioitu

Abstrakti

Electromagnetic and thermoelectric characteristics of a sodium-cobalt oxide, NaxCoO2, were investigated. A precise control of Na nonstoichiometry was successfully facilitated by an unusual synthesis method named "rapid heat-up" technique. With increasing x, the absolute value of resistivity (p) monotonically decreased, while the value of thermoelectric power (S) increased, giving rise to a drastic enhancement in the thermoelectric power factor, i.e. S2 / p. Simultaneously enhanced thermoelectric power and reduced resistivity of the present compound are difficult to be understood within the framework of a conventional band picture. Moreover, for samples with the solubility limit Na content, i.e. x = 0.75, we discovered an unconventional electronic transition at Tm = 22 K, which may be induced by the strong-correlation effect of 3d electrons.

AlkuperäiskieliEnglanti
Sivut425-430
Sivumäärä6
JulkaisuMaterials Research Society Symposium - Proceedings
Vuosikerta755
TilaJulkaistu - 10 marraskuuta 2003
OKM-julkaisutyyppiA4 Artikkeli konferenssijulkaisuussa
TapahtumaSolid-State Chemistry of Inorganic Materials - Boston, Yhdysvallat
Kesto: 2 joulukuuta 20026 joulukuuta 2002
Konferenssinumero: 4

Sormenjälki

Sukella tutkimusaiheisiin 'Electromagnetic and Thermoelectric Characteristics of Na xCoO2 of Precisely Controlled Na Nonstoichiometry'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä