Elastic, crosslinked poly(acrylic acid) filaments: Nanocellulose reinforcement and graphene lubrication

S. Spoljaric, A. Salminen, N. D. Luong, J. Seppälä*

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

8 Sitaatiot (Scopus)
51 Lataukset (Pure)

Abstrakti

Hybrid monofilaments of poly(acrylic acid) (PAA) and 1,6-hexanediol diglycidyl ether (16DGE), compounded with nanofibrillated cellulose (NFC) and graphene, were thermally crosslinked and subsequently spun from aqueous solution. Crosslinking, in the form of ester linkage formation, between PAA and 16DGE was successfully achieved via thermal induction. The monofilaments were elastic and flexible in nature, displaying remarkable elongation and work-to-break values (up to nine times higher than pure PAA-16DGE filaments). This unique behaviour derives from a synergy between the fillers; namely the reinforcing ability of cellulose nanofibrils and the lubricating effect of graphene.

AlkuperäiskieliEnglanti
Sivut107992-108001
Sivumäärä10
JulkaisuRSC Advances
Vuosikerta5
Numero130
DOI - pysyväislinkit
TilaJulkaistu - 7 joulukuuta 2015
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Sormenjälki Sukella tutkimusaiheisiin 'Elastic, crosslinked poly(acrylic acid) filaments: Nanocellulose reinforcement and graphene lubrication'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

  • Laitteet

  • Siteeraa tätä