Eco-friendly surface hydrophobization of all-cellulose composites using layer-by-layer deposition

O. Korhonen, N. Forsman, M. Österberg, T. Budtova*

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

1 Sitaatiot (Scopus)
137 Lataukset (Pure)

Abstrakti

All-cellulose composites were prepared by dispersing kraft fibers in a matrix made from pulp dissolved in NaOH-water. To hydrophobize the composite surface while maintaining the material fully bio-based and biodegradable, layer-by-layer deposition of cationic starch and carnauba wax was performed. Various options of surface coating, drying, and curing were tested, including partial and complete melting of the wax. The composite surface was characterized by water contact angle, roughness and scanning electron microscopy, and material properties by adsorption and absorption of water (in vapor and liquid form) and tensile testing. The highest water contact angle was obtained when the layer-by-layer deposition was performed by dipping the dry composite into cationic starch solution, then in wax dispersion, and partially melting the wax after coating. However, it was demonstrated that the dipping approach was detrimental to material tensile properties, due to heterogeneous swelling of cellulose during the treatment and multiple drying sequences. Process optimization via spraying resulted in composites with Young's modulus of 6 GPa and hydrophobic surface with water contact angle 122 degrees C.

AlkuperäiskieliEnglanti
Sivut896-907
Sivumäärä12
JulkaisuExpress Polymer Letters
Vuosikerta14
Numero10
DOI - pysyväislinkit
TilaJulkaistu - lokakuuta 2020
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Sormenjälki

Sukella tutkimusaiheisiin 'Eco-friendly surface hydrophobization of all-cellulose composites using layer-by-layer deposition'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä