Directional conductivity in layered alumina

Irina Hussainova*, Ali Saffar Shamshirgar, Roman Ivanov, Olga Volobujeva, Alexey E. Romanov, Michael Gasik

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

1 Sitaatiot (Scopus)

Abstrakti

Here we report a novel strategy to consolidate layered alumina demonstrating the directional electrical and thermal conductivity. The material was produced via incorporation of alumina nanofibers (20 ± 2 nm in diameter) decorated by several layers of graphene wrapped around longitudinal axes of the fibers. The graphenated fibers, obtained with the help of one-step catalyst-free CVD process, offered inhibition of grain growth combined with electrical conductivity to the sandwiched composites, which were consolidated by spark plasma sintering. Impact of the concentration of the fillers together with thickness of the conductive graphene-containing layer on thermal properties was studied. A graphene-containing interlayer with 50 μm thickness, sandwiched between two monolithic 10 mm layers of alumina shows ~30% enhancement in isotropic thermal conductivity of monolithic alumina.

AlkuperäiskieliEnglanti
Sivut68-73
Sivumäärä6
JulkaisuCurrent Applied Physics
Vuosikerta40
Varhainen verkossa julkaisun päivämäärä13 kesäk. 2020
DOI - pysyväislinkit
TilaJulkaistu - elok. 2022
OKM-julkaisutyyppiA1 Alkuperäisartikkeli tieteellisessä aikakauslehdessä

Sormenjälki

Sukella tutkimusaiheisiin 'Directional conductivity in layered alumina'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä