Differential scanning calorimetry/small-angle X-ray scattering analysis of ultraviolet sensible polypropylene filaments

Martina Vikova*, Shinichi Sakurai, Aravin Prince Periyasamy, Hidekazu Yasunaga, Miroslava Pechočiaková, Anna Ujhelyiová

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

Abstrakti

In this work, ultraviolet (UV) sensible metallocene isotactic polypropylene (miPP) filaments were produced with different drawing ratios and various concentrations of photochromic pigment. The effects of pigment concentration and drawing ratio on the chromatic properties and the structural modification for the miPP filaments were studied extensively by differential scanning calorimetry (DSC) and small- and wide-angle X-ray scattering (SAXS/WAXS) measurements. The change in melting temperature and the polymeric structures, such as lamellar thickness, long period and degree of crystallinity of miPP with the addition of a UV sensible pigment into miPP and the drawing process, were evaluated. The results show that the pigment concentration and the drawing ratio influence the inner structure of miPP filaments. Finally, our investigation shows that SAXS and also WAXS are appropriate to determine the lamellar thickness and the degree of crystallinity established by the DSC approach. This work attempts to correlate the results of lamellar thickness, the degree of crystallinity and the higher-order structure of the polymer acquired by DSC as well as X-ray diffraction (XRD) techniques in order to develop an appropriate approach to find the influence of pigment concentration and drawing ratio on miPP filaments.
AlkuperäiskieliEnglanti
Sivumäärä12
JulkaisuTextile Research Journal
Varhainen verkossa julkaisun päivämäärä18 lokakuuta 2021
DOI - pysyväislinkit
TilaSähköinen julkaisu (e-pub) ennen painettua julkistusta - 18 lokakuuta 2021
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Sormenjälki

Sukella tutkimusaiheisiin 'Differential scanning calorimetry/small-angle X-ray scattering analysis of ultraviolet sensible polypropylene filaments'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä