Defect detection in Fe-Cr alloys with positron annihilation doppler broadening spectroscopy

Veronika Sabelová*, Martin Petriska, Jana Veterníková, Vladimír Slugeň, Jarmila Degmová, Simo Kilpeläinen

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: Artikkeli kirjassa/konferenssijulkaisussaConference contributionScientificvertaisarvioitu

2 Sitaatiot (Scopus)

Abstrakti

Positron annihilation Doppler broadening spectroscopy (DBS) has been used for the detection of structural defects in Fe-9wt%Cr (Fe-9Cr) alloy in the as-prepared and implanted states. Defects were created by He and H ion implantation with a kinetic energy of 250 keV. DBS is a nondestructive method and is a unique tool for the observation of open volume defects like vacancies and vacancy clusters in solids. A positron beam with variable positron energy was used for the measurement of defect depth profiles up to 1.5 μm. The obtained results provide qualitative and semi-quantitative information about radiation induced defects and their chemical environment. Although the collision damage from helium implantation was one order of magnitude higher than for the case of hydrogen, the changes in S and W parameters are much less significant, probably due to considerably lower mobility of helium in the implanted materials, which results in helium capture by the created open volume defects.

AlkuperäiskieliEnglanti
OtsikkoPositron and Positronium Chemistry X
Sivut270-273
Sivumäärä4
Vuosikerta733
DOI - pysyväislinkit
TilaJulkaistu - 2013
OKM-julkaisutyyppiA4 Artikkeli konferenssijulkaisuussa
TapahtumaInternational Workshop on Positron and Positronium Chemistry - Smolenice Castle, Smolenice, Slovakia
Kesto: 5 syyskuuta 20119 syyskuuta 2011
Konferenssinumero: 10

Julkaisusarja

NimiMaterials Science Forum
Vuosikerta733
ISSN (painettu)02555476

Conference

ConferenceInternational Workshop on Positron and Positronium Chemistry
LyhennettäPPC
MaaSlovakia
KaupunkiSmolenice
Ajanjakso05/09/201109/09/2011

Sormenjälki Sukella tutkimusaiheisiin 'Defect detection in Fe-Cr alloys with positron annihilation doppler broadening spectroscopy'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä