Corrosion protection of steel with multilayer coatings: Improving the sealing properties of physical vapor deposition CrN coatings with Al2O3/ TiO2 atomic layer deposition nanolaminates

Tutkimustuotos: Lehtiartikkelivertaisarvioitu

Tutkijat

Organisaatiot

Kuvaus

Atomic Layer Deposition (ALD) of Al2O3/TiO2 nanolaminatewas applied to improve the sealing properties of CrN coating deposited with Physical Vapor Deposition (PVD) on high speed steel (HSS). The corrosion protection propertieswere explored with Linear Sweep Voltammetry and visual estimation. Nearly two orders of magnitude decrease in corrosion current density was obtained by applying plasma pre-treatment prior to ALD coating. Sealing of CrN pinholes was shown with Focused Ion Beam/Scanning Electron Microscope technique. The effect of the ALD deposition parameters to adhesion of the ALD coatings was investigated with Rockwell indentation and microscope analysis. Thickness and refractive index of the ALD coatings were measured with ellipsometry, and density and roughness of the ALD coatingswere investigatedwith X-Ray Reflectivity measurements. Neutral Salt Spray testing was used to investigate the corrosion resistance of PVD/ALD nanolaminates on HSS dental curettes.

Yksityiskohdat

AlkuperäiskieliEnglanti
Sivut59-68
Sivumäärä10
JulkaisuThin Solid Films
Vuosikerta627
Varhainen verkossa julkaisun päivämäärä24 helmikuuta 2017
TilaJulkaistu - huhtikuuta 2017
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Lataa tilasto

Ei tietoja saatavilla

ID: 11232481