Coking resistant Ni–La0.8Sr0.2FeO3 composite anode improves the stability of syngas-fueled SOFC

Xueli Yao, Muhammad Imran Asghar*, Yicheng Zhao, Yongdan Li, Peter D. Lund

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

5 Sitaatiot (Scopus)

Abstrakti

An improved SOFC anode with excellent stability against carbon deposition with syngas as fuel is reported. The anode material is Ni–La0.8Sr0.2FeO3 (LSF) composite synthesized by anhydrous impregnation. After reduction in wet H2 (3% H2O), the material partially decomposes to SrLaFeO4 and exsolved Fe. The exsolved Fe forms Ni–Fe alloy with impregnated Ni. The particle size of Ni–Fe alloy is about 20–50 nm. The Ni–Fe alloy nanoparticles disperse on the surface of the La0.8Sr0.2FeO3 and SrLaFeO4 oxides. The increase of Ni content promotes the exsolution of Fe and increases the reaction sites of Ni–Fe alloy. With the increase of the Ni content, the electrical conductivity and catalytic activity are enhanced, which improves the electrochemical performance of the single cell. The cell with 10 mol.% Ni impregnated Ni-LSF as anode achieves a maximum power density of 550 mW cm−2 at 700 °C fueled with syngas. The strong interaction of the nano-sized Ni–Fe alloy with the LaxSryFeOz (La0.8Sr0.2FeO3 or SrLaFeO4) oxide substrate efficiently suppresses carbon deposition with high graphitization degree. Besides, the SrLaFeO4 phase which can accommodate interstitial oxygen facilitates the removal of the deposited carbon.

AlkuperäiskieliEnglanti
Sivut9809-9817
Sivumäärä9
JulkaisuInternational Journal of Hydrogen Energy
Vuosikerta46
Numero15
Varhainen verkossa julkaisun päivämäärä1 tammik. 2020
DOI - pysyväislinkit
TilaJulkaistu - 26 helmik. 2021
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Sormenjälki

Sukella tutkimusaiheisiin 'Coking resistant Ni–La0.8Sr0.2FeO3 composite anode improves the stability of syngas-fueled SOFC'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä