Chemical ageing effects on the ply and laminate strength of a filament wound cross-ply GFRP

O. Rodera*, T. Pärnänen, J. Jokinen, M. Lindgren, E. Sarlin, M. Kanerva

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

16 Lataukset (Pure)

Abstrakti

This work presents a numerical approach to multi-routines based on experiments, and, with a target to analyse strength of a cross-ply glass fibre reinforced plastics (GFRP) composite after immersion in sulphuric acid solution under pressure (5% H2SO4 solution, 95 °C, 15 bar). Two alternative vinyl ester resins (bisphenol A diglycidyl ether and epoxy phenol novolac) were investigated. After 0.5, 1, 1.5 and 2 years of conditioning, the specimens were mechanically tested. The multi-scale definition of the material system and its virtual conditioning were performed in a finite element (FE) model. The Hashin 3D failure criterion was implemented by coding the UMAT subroutine when using the Abaqus software. The experimental results demonstrated better performance of the bisphenol A vinyl ester resin-based GFRP when a thin barrier layer is used. The numerical results indicated that the shear strength property was the most susceptible at weak zones to present a tendency for degradation after one year of conditioning.

AlkuperäiskieliEnglanti
Artikkeli113508
Sivumäärä15
JulkaisuComposite Structures
Vuosikerta260
Varhainen verkossa julkaisun päivämäärä25 joulukuuta 2020
DOI - pysyväislinkit
TilaJulkaistu - 15 maaliskuuta 2021
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Sormenjälki Sukella tutkimusaiheisiin 'Chemical ageing effects on the ply and laminate strength of a filament wound cross-ply GFRP'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä