Characterization and performance of diamond-like carbon films synthesized by plasma- and ion-beam-based techniques

Tutkimustuotos: Lehtiartikkeli

Tutkijat

  • K. C. Walter
  • H. Kung
  • T. Levine
  • J. T. Tesmer
  • P. Kodali
  • B. P. Wood
  • D. J. Rej
  • M. Nastasi
  • Jari Koskinen

  • J. P. Hirvonen

Organisaatiot

  • VTT Technical Research Centre of Finland
  • Los Alamos National Laboratory

Kuvaus

Diamond-like carbon (DLC) films have been deposited on dissimilar substrates using three different deposition processes. Two well-studied deposition methods, employing cathodic arcs and r.f. plasma self-bias, have been used. These two processes differ in that cathodic arc processes use gas pressures less than 1 mTorr (0.13 Pa) and deposit atomic ions with energies less than 100 eV, while r.f. plasma self-bias processes use gas pressures greater than 1 mTorr (0.13 Pa) and deposit molecular ions with energies greater than 100 eV. In addition, DLC films have been deposited using a new plasma-based, pulsed-bias process. The pulsed-bias process uses gas pressures greater than 1 mTorr (0.13 Pa) and deposits molecular ions with energies greater than 1000 eV. Both the self-bias and the pulsed-bias processes utilized hydrocarbon gases as the carbon source. Cathodic arc processes generally rely on the arc between two graphite electrodes as the carbon source. Deposited films from all three processes have been characterized using ion backscattering techniques, elastic recoil spectrometry, transmission electron microscopy (TEM) and selected-area diffraction. Films deposited using the cathodic arc process are virtually hydrogen free while the self-bias and pulsed-bias films contain up to 40% H. TEM results indicated that the films are homogeneous and amorphous. The hardness, elastic modulus, coefficient of friction and wear rate of the films are also reported.

Yksityiskohdat

AlkuperäiskieliEnglanti
Sivut734-738
Sivumäärä5
JulkaisuSurface and Coatings Technology
Vuosikerta74-75
NumeroPart 2
TilaJulkaistu - lokakuuta 1995
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

ID: 4320327